ALAMBRE AUTROD 308LSI 0.8MM x 5 K (742431)

Rubro: ALAMBRE ESPECIALES Marca: ESAB

A continuous solid corrosion resisting chromium-nickel wire for welding of austenitic chromium nickel alloys of 18% Cr - 8% Ni-type. OK Autrod 308LSi has a good general corrosion resistance. The alloy has a low carbon content making it particularly recommended where there is a risk of intergranular corrosion. The higher silicon content improves the welding properties, such as wetting. The alloy is widely used in the chemical and food processing industries as well as for pipes, tubes and boilers

---

Caracteristicas

Propiedades típicas de Tensión

Alargamiento	Condición	Límite de flujo	Resistencia a la tracción	Gas de protección
36 %	As Welded	400 MPa	570 MPa	-
25 %	As Welded	370 MPa	490 MPa	Tested at 350°C.

Teste Charpy

Condición	Temperatura de prueba	Valor de impacto
As Welded	20 °C	110 J
As Welded	-60 °C	70 J
As Welded	-196 °C	45 J

Composición química

wire composition
Mn	Mo	Cu	C	Si	Ferrite FN	Ni	Cr
1.8 %	0.15 %	0.10 %	0.01 %	0.9 %	9 %	10.5 %	19.9 %

Depósito

Diámetro	Corriente	Tasa de Deposición	Tensión	Velocidad de Alimentación
0.6 mm	-	-	-	-
0.8 mm	55-160 A	1.0-4.1 kg/h	15-24 V	4.0-17.0 m/min
0.9 mm	65-220 A	1.1-5.4 kg/h	15-28 V	3.5-18.0 m/min
1.0 mm	80-240 A	1.5-6.0 kg/h	15-28 V	4.0-16.0 m/min
1.14 mm	-	-	-	-
1.2 mm	100-300 A	1.6-7.5 kg/h	15-29 V	3.0-14.0 m/min
1.6 mm	230-375 A	5.2-8.6 kg/h	23-29 V	5.5-9.0 m/min

Aprobaciones:	BV; 308L SA BT (M12); CE; EN 13479; CWB; ER308LSi; DB; 43.039.01; DNV-GL; VL 308 L (M13); NAKS/HAKC; 0.8-1.2 mm; VdTÜV; 04267
Clasificaciones:	EN ISO 14343-A; G 19 9 L Si; Wire Electrode; SFA/AWS A5.9; ER308LSi; Wire Electrode; Werkstoffnummer; ~1.4316; Wire Electrode

Aprobaciones vinculadas a la planta de producción. Para obtener más información, pongase en contacto con ESAB.

tipo de aleación:

Austenitic (with approx. 8 % ferrite)  19% Cr - 9% Ni - Low C - High Si