Shield-Bright 316L was developed for the welding of Type 316L stainless steel but can be used for other stainless steels including Types 316 and 304L. In a few cases, e.g. nitric acid service, Shield-Bright 316L should not be used to weld 304L. It contains molybdenum which resists pitting corrosion induced by sulphuric and sulphurous acids, chlorides and cellulose solutions. Used widely in the rayon, dye and paper making industries.
Propiedades típicas de Tensión
| Alargamiento | Condición | Límite de flujo | Resistencia a la tracción | Gas de protección |
| 37 % | As Welded | 400 MPa | 560 MPa | - |
| 26 % | As Welded | 340 MPa | 440 MPa | Tested at 350°C. |
Teste Charpy
| Condición | Temperatura de prueba | Valor de impacto |
| As Welded | 20 °C | 120 J |
| As Welded | -60 °C | 95 J |
| As Welded | -110 °C | 70 J |
| As Welded | -196 °C | 45 J |
Composición química
|
| wire composition |
| Mn | Mo | Cu | C | Si | Ferrite FN | Ni | Cr |
| 1.8 % | 2.60 % | 0.12 % | 0.01 % | 0.9 % | 7 % | 12.2 % | 18.4 % |
Depósito
| Diámetro | Corriente | Tasa de Deposición | Tensión | Velocidad de Alimentación |
| 0.6 mm | - | - | - | - |
| 0.8 mm | 55-160 A | 1.0-4.1 kg/h | 12-24 V | 4.0-17.0 m/min |
| 0.9 mm | 65-220 A | 1.1-5.4 kg/h | 15-28 V | 3.5-18.0 m/min |
| 1.0 mm | 80-240 A | 1.5-6.0 kg/h | 15-28 V | 4.0-16.0 m/min |
| 1.14 mm | - | - | - | - |
| 1.2 mm | 100-300 A | 1.6-7.5 kg/h | 15-29 V | 3.0-14.0 m/min |
| 1.6 mm | 230-375 A | 5.2-8.6 kg/h | 23-31 V | 5.5-9.0 m/min |
| Aprobaciones: | CE; EN 13479; CWB; ER316LSi; DB; 43.039.05; DNV-GL; VL 316 L (M13); VdTÜV; 04268; NAKS/HAKC; 0.8-1.2 mm |
| Clasificaciones: | EN ISO 14343-A; G 19 12 3 L Si; Wire Electrode; SFA/AWS A5.9; ER316LSi; Wire Electrode; Werkstoffnummer; ~1.4430; Wire Electrode |
Aprobaciones vinculadas a la planta de producción. Para obtener más información, pongase en contacto con ESAB.
| tipo de aleación: | Austenitic (with approx. 8 % ferrite) 19% Cr - 12% Ni - 3% Mo - Low C - High Si |